磨玻璃增強阻燃尼龍66 LNP THERMOCOMP RFZ349XC
PA66 基礎創新塑料(美國) RFZ349XC BKIA800
磨制玻璃|玻纖增強 阻燃性能(RF-1007 FR MG LEX)LNP THERMOCOMP * RFZ349XC 尼龍66樹脂復合含20%玻璃纖維,15%磨玻璃。這種材料額外的特性包括:阻燃。
物理性能：
| Density | 1.66 g/cc | 0.0600 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.430 % | 0.430 % | 23°C / 50% RH; ISO 62 | |
Linear Mold Shrinkage, Flow 
|
0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
|
0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
|
Linear Mold Shrinkage, Transverse
|
0.0119 cm/cm @Time 86400 sec |
0.0119 in/in @Time 24.0 hour |
ISO 294 |
|
0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
機械性能：
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| 124 MPa | 18000 psi | ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 |
| 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 197 MPa | 28600 psi | ISO 178 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m2 | 18.6 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |