導電阻燃尼龍66 LNP STAT-KON RE0029
PA66 美國液氮 RE-0029 BK8115
碳纖維增強材料 添加 阻燃劑 性能特點 導電尼龍 阻燃尼龍LNP * stat-kon re0029是一種化合物，以尼龍66樹脂含有10%的碳纖維。這種材料增加的功能包括：導電，阻燃。
機械性能：
| Tensile Strength at Break | 126 MPa | 18300 psi | ISO 527 |
| 131 MPa | 19000 psi | ASTM D638 | |
| Tensile Strength, Yield | 126 MPa | 18300 psi | ISO 527 |
| 131 MPa | 19000 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Elongation at Yield | 1.6 % | 1.6 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 10.21 GPa | 1481 ksi | 1 mm/min; ISO 527 |
| 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 186 MPa | 27000 psi | ISO 178 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.29 J/cm | 24.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m2 | 11.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |