30%玻璃珠增強PA66 美國LNP RB006
PA66 美國液氮 RB006 WHNAT
玻璃珠填充增強材料
SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66
LNP* THERMOCOMP* RB006 含30%玻璃微珠填充的尼龍66樹脂的化合物。
物理性能：
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.36 g/cc | 0.0491 lb/in3 | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.720 % | 0.720 % | 50% RH, 24 hrs; ASTM D570 |
| 0.720 % | 0.720 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow |
>= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
機械性能：
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| 66.0 MPa | 9570 psi | ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 | |
| 7.6 % | 7.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.81 GPa | 988 ksi | 50 mm/min; ASTM D638 |
| 7.28 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 87.0 MPa | 12600 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 124 MPa | 18000 psi | ASTM D790 | |
| Flexural Modulus | 3.84 GPa | 557 ksi | 2 mm/min; ISO 178 |
| 4.05 GPa | 587 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 4.69 GPa | 680 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 | 1.43 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m2 | 11.9 ft-lb/in2 | 80*10*4; ISO 180/1U |