首先，現今各大鋼廠生產SUS315J2合金都引用以下鍛造標準：

  SUS315J2棒材：  

ASTM B 446; ASME SB 446 (Rod & Bar), 

AMS 5666 (Bar, Forgings, & Rings); 

ISO 9723 (Rod & Bar), 

VdTÜV 499 (Rod & Bar), 

BS 3076NA21 (Rod & Bar), 

EN 10095 (Rod, Bar, & Sections), 

DIN 17752 (Rod & Bar), 

ASME Code Case 1935 (Rod, Bar, & Forgings), 

  SUS315J2線材：  

DIN 17753 (Wire). 

ISO 9724 (Wire) 

AMS 5837 (Wire), 

  SUS315J2鍛件：  

ISO 9725 (Forgings), 

ASTM B 564; ASME SB 564 (Forgings); 

DIN 17754 (forgings), 

  SUS315J2板材：  

ASTM B 443; ASTM SB 443 (Plate, Sheet & Strip), 

AMS 5599; 5869; MAM 5599 (Plate, Sheet & Strip), 

ISO 6208 (Plate, Sheet & Strip), 

VdTÜV 499 (Plate, Sheet & Strip), 

BS 3072NA21 (Plate & Sheet), 

EN 10095 (Plate, Sheet & Strip), 

DIN 17750 (Plate, Sheet & Strip), 

ASME Code Case 1935. 

  SUS315J2管材：  

ASTM B 444; ASTM B 829; 

ASME SB444; ASME SB 829 (Seamless Pipe & Tube), 

ASTM B704; ASTM B 751; ASME SB 704; 

ASME SB 751 (Welded Tube), 

ASTM B705; ASTM B 775; ASME SB 705; 

ASME SB 775 (Welded Pipe), 

ISO 6207 (Tube), 

AMS 5581 (Seamless & Welded Tube), 

VdTÜV 499 (Tube), 

BS 3074NA21 (Seamless Pipe & Tube), 

DIN 17751 (Tube), 

ASME Code Case 1935.

---------------------------------------

  其次，鎳基高溫合金的顯微組織即各組成相特別是析出相的性質、形態、大小、含量及分布決定了其高溫力學性能及運行壽命。然而，合金的組織狀態是由其成分所決定的。因此，決定合金性能的源頭在于合金成分本身，即構成合金成分的各元素的種類及其含量。讓我們來看下SUS315J2合金成分：

SUS315J2

SUS315J2不銹鋼

不銹鋼：SUS315J2

標準：JIS

●SUS315J2特性應用：

●SUS315J2化學成分：

碳 C：≤0.08

錳 Mn：≤2.00

鎳 Ni：11.00~14.00

硅 Si：2.50~4.00

磷 P：≤0.045

硫 S：≤0.030

鉻 Cr：17.00~20.50

鉬 Mo：0.50~1.50

●力學性能：   

抗拉強度 σb (MPa)：≥520

條件屈服強度 σ0.2 (MPa)：≥205   

伸長率 δ5 (%)：≥40   

硬度：≤200HV 

  從SUS315J2成分中發現需要有較高含量的易氧化合金元素如鉻、鉬、鈷、鈦等強化元素，這些易氧化元素合金和鎳金屬本身成為合金中有害雜質元素特別是硫、磷的重要來源，鎳基高溫合金中要求有害雜質元素S和P的含量小于0.010-0.020%。