品名 |
AWS型號 |
產品牌號 |
特性簡單介紹 |
|
不銹鋼焊條 |
E308L-15 |
FROINOX |
C:≤0.040,Si:≤0.40,Mn:1.3,Ni:10.0,Cr:20.0,Mo≤0.20,σb:≥520,σs:≥350,δ5:≥35%,Akv:≥80(+20℃)，α相:4-8%,抗裂性能和機械性能優良 |
|
E308L-16 |
SAFINOX RCN18.8S |
C:0.025,Si:0.6,Mn:1.3,Ni:10.2,Cr:19.2,σb:550,σs:390,δ5:42%,Akv:45(-100) ℃,α相：8%，力學性能和焊接工藝性能優良，特別適合管道焊接 |
|
|
E316-15 |
SAFINOX B CND 316 |
C:0.06,Si:0.6,Mn:1.80,Ni:12.5,Cr:18.5,Mo:2.2,σb:610,σs:450,δ5:35%,Akv:90(+20℃),α相：8%，抗裂性能和機械性能優良，特別適合管道焊接 |
|
|
E316L-16 |
SAFINOXR CND18.8.3S |
C:0.022,Si:0.6,Mn:1.3,Ni:12,Cr:19.2,Mo:2.2,σb:570,σs:430,δ5:38%,Akv:40(-101℃),α相:7%,力學性能和工藝性能優良，特別適合管道焊接 |
|
|
E316L-17 |
SAFFINOXR CND316L |
C:0.018,Si:0.85,Mn:0.8,Ni:11.5,Cr:18.5,Mo:2.8,σb:590,σs:400,δ5:39%,Akv:40(-101℃),α相:9%,力學和工藝性能優良，無飛濺，自動脫渣，表面平整光潔 |
|
|
E309L-15 |
FROINOX E309L-15 |
C:≤0.04,Si:0.7,Mn:1.0,Ni:13.0,Cr:23.0,Mo:≤0.5,σb:≥520,σs:≥350,δ5:≥30%,Akv:≥60(20℃),α相：8—13%,抗裂性能優良，焊接相應級別的不銹鋼或異種鋼 |
|
|
E309L-16 |
SAFINOX R CN24.12S |
C:0.025,Si:0.5,Mn:1.4,Ni:13,Cr:23.5,σb:580,σs:460,δ5:35%,Akv:55(20℃),σ相:9%,性能優良，焊接或堆焊相應級別的不銹鋼或異種鋼 |
|
|
E310-16 |
SAFINOX RCN25.20 |
C:0.10,Si:0.75,Mn:1.70,Ni:21.0,Cr:27.0,σb:580,σs:30%,Akv:65(+20℃)，純奧氏體不銹鋼焊條，性能優良，焊接相應級別的不銹鋼 |
|
|
E2209-16,-17 |
LEXAL 22.9.3 N HR |
C:0.016,Si:1.0,Mn:1.6,Ni:9.0,Cr:22.8,Mo:3.2,N:0.16,σb:810,σs:700,δ5:22%,Akv:50(-40℃),σ相:40%,雙相鋼焊條，抗拉強度高，抗點腐蝕和抗CI離子腐蝕性能優良 |
|
|
E317-16 |
FRO INOX E 317-16 |
C:≤0.08,Si:0.70,Mn:1.00,Ni:13.Cr:20,Mo:3.5,σb: ≥550,σs:≥400,δ5≥30%,Akv:≥28(+20℃),α相:5-10%焊接工藝性能良好，用于焊接AISI317不銹鋼 |
|
|
E347-16 |
SAFINOX RCN 347 |
C:0.02,Si:0.9,Mn:0.85,Ni:10.3,Cr:20.0,Nb:0.7,σb:650,σs:490,δ5:33%,Akv:75(+20℃),α相:10%，工藝性能優良，焊接含或不含Ti.,Nb奧氏體不銹鋼 |
|
|
E410-15 |
FRO CROM 13/L |
C:≤0.08,Si:≤0.90,Mn:≤1.0,Cr:12.0,Ni:≤0.60,Mo:≤0.5,σb:≥450,δ5:≥50%,Akv:≥47(0℃),用于焊接13%Cr的鐵素體-馬氏體 |
|
|
E385-15 |
SAFINOXR CNDU 20.25.5.S |
C:0.02,Si:0.4,Mn:1.3,Ni:25.,Cr:20,Mo:4,Cu:1.7,σb:550,σs:370,δ5:35%,Akv:70(+20℃),純奧氏體不銹鋼焊條，抗熱硫酸，冷鹽酸，和點腐蝕性能非常好，焊接904等不銹鋼 |
不銹鋼及鎳基合金實芯焊絲
|
AWS型號 |
產品牌號 |
焊絲典型化學成份 |
|||||||||
|
|
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
Nb |
Cu≤ |
N≤ |
Co≤ |
|
ER308L |
NERTALINOX 308L |
0.01 |
0.4 |
1.7 |
20.0 |
10.0 |
|
|
|
|
|
|
ER308LSi |
NERTALIC 50 |
0.01 |
0.8 |
1.7 |
20 |
10 |
|
|
0.15 |
0.06 |
0.10 |
|
ER309Si |
FILINOX 309 LSi |
≤0.03 |
0.8 |
1.8 |
24 |
13 |
|
|
|
|
|
|
ER309LMo |
FILINOX 309LMo |
≤0.03 |
0.4 |
1.5 |
24 |
13 |
2.7 |
|
|
|
|
|
ER316LSi |
NERTALIC 52HP |
<0.01 |
0.8 |
1.7 |
17.5 |
14.5 |
2.3 |
|
0.15 |
0.06 |
0.10 |
|
ER347Si |
NERTALIC 53 |
0.06 |
0.85 |
1.7 |
20 |
10 |
|
0.7 |
|
|
|
|
ER2209 |
LEXAL G 22.9.3. |
0.03 |
0.5 |
1.6 |
22.8 |
8.5 |
3 |
|
|
0.2 |
|
|
ER Ni Cr3 |
NERTALIC 210 |
0.01 |
0.15 |
3 |
20 |
72.5 |
|
2.5 |
Fe(0.7) |
||
|
焊接鎳基合金，鑄鐵，不銹鋼與碳鋼，淬火傾向大的難焊鋼種 |
|||||||||||
|
ERNiCr Mo-3 ERNiCr Mo-4 |
NERTALIC 625 AS 276 |
0.03 |
0.2 |
0.3 |
22 |
余量 |
9 |
3．5 |
Fe(4.0) |
|
|
|
焊接或堆焊鎳基合金，高Cr,Ni合金，防海水腐蝕，耐高溫（1000℃）和低溫（-196℃）性能優良，焊接5%-9%Ni鋼等 |
|||||||||||
碳鋼，低合金鋼實芯焊絲和焊棒
|
AWS型號 |
產品牌號 |
焊絲化學成份 |
特性簡單介紹 |
||||||
|
|
|
C |
Mn |
Si |
S |
P |
|
|
|
|
ER70S-3 |
NERTALIC 70S |
0.08 |
1.15 |
0.6 |
0.015 |
0.015 |
|
|
|
|
ER70S-6 |
NERTALIC 70A |
0.08 |
1.4 |
0.8 |
0.015 |
0.015 |
|
|
|
|
ER80SG |
CARBOFIL Cr Mo 1 |
0.08 |
1.4 |
0.8 |
|
Mo:0.6 Cr:1.1 |
焊接σs≥420Mpa高強鋼 |
||
|
ER110S-G |
NERTALIC 88 |
0.05 |
1.9 |
0.45 |
0.010 |
0.010 |
Ni:2.0 Mo:0.55 |
焊接σs≥650Mpa高強鋼，用于ELDOX 700鋼，WEDOX900低強匹配焊 |
|
|
ER100S-G |
CARBOFIL Ni Mo Cr |
≤0.01 |
1.6 |
0.6 |
|
Ni:1.4,Mo:0.25,Cr:0.3 |
焊接σs≥690Mpa高強鋼，用于WELDOX 700鋼，WEDOX900低強匹配焊 |
||
|
ER90S-G |
CARBOFIL Ni Mo 1 |
≤0.10 |
1.8 |
0.6 |
|
|
Ni:1.0 Mo:0.4 Ti:0.15 |
焊接σs≥620Mpa高強鋼 |
|
|
ER120S-G |
ED-FK 1000 |
0.10 |
1.80 |
0.80 |
|
Mo:0.50,Ni:2.20 |
焊接σs≥620Mpa高強鋼，用于WELDOX900，960鋼 |
||
|
ER90S-B3 |
OE CrMo2 |
0.08 |
1.1 |
0.6 |
|
|
Cr:2.7 Mo:1.0 |
焊接2.25%Cr-1%Mo耐熱鋼 |
|
|
ER90S-B9 |
OE-CrMo91V |
0.10 |
0.50 |
Si:0.4,Cr:11.5,Mo:1.0,W:0.5,V:0.3 |
|
9Cr1MoV(P91,T91)耐熱鋼焊接 |
|||
碳鋼（MIG/MAG）藥芯焊絲
|
AWS型號 |
產品牌號 |
主要力學性能 |
特性簡單介紹 |
||
|
|
|
σb(MPa) |
σs(MPa) |
AKV(J) |
|
|
E71T1 |
OT100/SAFDUAL 100 |
580 |
515 |
90(-20℃) |
包括立向上（擺動或不擺動），立向下的全位置焊接，焊縫非常平滑 |
|
E71T1-G |
FLUXOFIL 18 |
520-620 |
≥430 |
≥80(-20℃) |
Ni:1.2,Cu:0.5,焊接耐大氣腐蝕鋼，焊接工藝性能優良 |
|
E71T5 |
SAFDUAL 31 |
580 |
490 |
90(-20℃) |
鍍銅焊絲，適合遠距離送絲 |
|
E71T-GS |
SAFDUAL ZN |
|
|
|
Al:2.2,自動生產線，空調機，和鋼結構的鍍鋅板和薄板焊接 |
|
E70C-GS E70T2 |
SAFDUAL TGV |
|
|
|
高速自動氣保護藥芯焊絲，焊接電流可用到650A，焊接速度4.7m/min.主要用于水箱，滅火器，壓縮機，車廂，等結構的焊接，可焊接鍍鋅板，13%Cr等鋼 |
低合金鋼（MIG/MAG）藥芯焊絲
|
AWS型號 |
產品牌號 |
主要力學性能 |
特性簡單介紹 |
||
|
E81T1-W |
FLUXOFILCORD 48/S |
580 |
≥470 |
≥47（-20℃） |
Cu:0.5,Cr:0.6,Ni:0.6,焊接腐蝕的高強鋼，適合單道和多道焊 |
|
E81T5Ni1 |
SAFDUAL 202 |
620 |
540 |
80（-60℃） |
含Ni:0.9%,低溫（-60℃）沖擊性能優良，適合全位置焊接，焊縫背面融合良好 |
|
E90T5-G |
FLUXOFIL43.1 |
550-650 |
≥430 |
≥40（-20℃） |
Mo:0.3,Ni:2.0,V:0.1,焊接高強鋼，焊接工藝性能優良 |
|
E91T5-B3 |
FLUXOFIL 37STC |
550-650 |
≥450 |
120（-20℃） |
Cr:2.3%,Mo:1.0%,焊接2.25Cr-1Mo鋼，雜質含量低，焊接步冷熱處理耐熱鋼 |
|
E110T5-K4 |
FLUXOFIL M142 |
800 |
≥680 |
≥27（-51℃） |
Mo:0.4%,Ni:2.0,Cr:0.4金屬粉芯無縫藥芯焊絲，工藝性能與FLUXOFIL M8相近，低溫沖擊性能優良 |
|
E120T5-G |
FLUXFILCORD 45 |
1000 |
≥900 |
47（-40℃） |
Ni:1.8%,Mo:0.4%,Cr:1.0%，高強鋼藥芯焊絲，低溫沖擊性能和抗裂性能非常好 |
低合金鋼（MIG/MAG）藥芯焊絲
|
AWS型號 |
產品牌號 |
主要力學性能 |
特性簡單介紹 |
||
|
E81T1-W |
FLUXOFILCORD 48/S |
580 |
≥470 |
≥47（-20℃） |
Cu:0.5,Cr:0.6,Ni:0.6,焊接腐蝕的高強鋼，適合單道和多道焊 |
|
E81T5Ni1 |
SAFDUAL 202 |
620 |
540 |
80（-60℃） |
含Ni:0.9%,低溫（-60℃）沖擊性能優良，適合全位置焊接，焊縫背面融合良好 |
|
E90T5-G |
FLUXOFIL43.1 |
550-650 |
≥430 |
≥40（-20℃） |
Mo:0.3,Ni:2.0,V:0.1,焊接高強鋼，焊接工藝性能優良 |
|
E91T5-B3 |
FLUXOFIL 37STC |
550-650 |
≥450 |
120（-20℃） |
Cr:2.3%,Mo:1.0%,焊接2.25Cr-1Mo鋼，雜質含量低，焊接步冷熱處理耐熱鋼 |
|
E110T5-K4 |
FLUXOFIL M142 |
800 |
≥680 |
≥27（-51℃） |
Mo:0.4%,Ni:2.0,Cr:0.4金屬粉芯無縫藥芯焊絲，工藝性能與FLUXOFIL M8相近，低溫沖擊性能優良 |
|
E120T5-G |
FLUXFILCORD 45 |
1000 |
≥900 |
47（-40℃） |
Ni:1.8%,Mo:0.4%,Cr:1.0%，高強鋼藥芯焊絲，低溫沖擊性能和抗裂性能非常好 |